Ti-6Al-2Sn-4Zr-2Mo Ti Alloy
Ti-6Al-2Sn-4Zr-2Mo Ti Alloy Ti Alloy and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
| Category | Type | Steel Grade | Standard | Country | Application |
|---|---|---|---|---|---|
| Steel Grades | Ti Alloy | Ti-6Al-2Sn-4Zr-2Mo Ti Alloy | |||
| DIN 1.0909 Ti Alloy | |||||
| Ti-8Mo-8V-2Fe-3Al Ti Alloy | |||||
| Ti-8Mn Ti Alloy | |||||
| Ti-8Al-1Mo-1V Ti Alloy | |||||
| Ti-7AI-4Mo Ti Alloy | |||||
| Ti-6Al-6V-2Sn-0.75Cu Ti Alloy | |||||
| Ti-6Al-4V-ELI (low O2) Ti Alloy | |||||
| Ti-6Al-4V Ti Alloy | |||||
| Ti-6Al-2Sn-l.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy | |||||
| Ti-6Al-2Sn-4Zr-6Mo Ti Alloy |
Chemical composition(mass fraction)(wt.%) of the Ti-6Al-2Sn-4Zr-2Mo Ti Alloy
Ti-6Al-2Sn-4Zr-2Mo Ti Alloy
Our advantages
Ti-6Al-2Sn-4Zr-2Mo properties and heat treatment forged piece, Including Ti-6Al-2Sn-4Zr-2Mo application and specifications, We have all specifications，Including Ti-6Al-2Sn-4Zr-2Mo steel plate, Ti-6Al-2Sn-4Zr-2Mo sheet, Ti-6Al-2Sn-4Zr-2Mo square steel, Ti-6Al-2Sn-4Zr-2Mo flat bar,Ti-6Al-2Sn-4Zr-2Mo round bar,Ti-6Al-2Sn-4Zr-2Mo forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the Ti-6Al-2Sn-4Zr-2Mo has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer’s requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer’s requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer’s requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer’s requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade Ti-6Al-2Sn-4Zr-2Mo and Standards
| Category | Titanium Alloy |
| Class | Wrought |
| Type | Near alpha alloy |
| Designations | United States: MIL-T-9046, AMS 4975 |
| Composition |
|
| Mechanical Properties |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 4.54 | 25 | |
| Poisson’s Ratio | 0.33 | 25 | |
| Elastic Modulus (GPa) | 113.8 | 25 | |
| Tensile Strength (Mpa) | 703 | 425 more | duplex annealed |
| Yield Strength (Mpa) | 586 | ||
| Elongation (%) | 21 | ||
| Reduction in Area (%) | 55 | ||
| Hardness (HRC) | 32 | 25 | duplex annealed |
| Thermal Properties |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Thermal Expansion (10-6/ºC) | 7.7 | 20–100 more | |
Machining performance
Download Ti-6Al-2Sn-4Zr-2Mo the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A–Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
Copyright © 1996-2011 Longhai Special Steel. All Rights Reserved.
Longhai steel is China’s special steel inventory spot suppliers. 
Stainless Steel | Mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free-cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high-temperature alloy | Low alloy high-temperature steel
Mechanical Properties of steel grade Ti-6Al-2Sn-4Zr-2Mo Ti Alloy
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 273 (≥) | 667 (≥) | 22 | 31 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 333 |
Physical Properties of steel grade Ti-6Al-2Sn-4Zr-2Mo Ti Alloy
| Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
|---|---|---|---|---|---|---|---|
| 12 | – | – | 0.33 | – | |||
| 133 | 398 | – | 14.3 | 132 | – | ||
| 282 | – | 32 | 33.2 | 123 | 212 |
Heat Treatment of steel grade Ti-6Al-2Sn-4Zr-2Mo Ti Alloy
Heat treated : 1585°C – 1522°C
Technological Curves of steel grade Ti-6Al-2Sn-4Zr-2Mo Ti Alloy
Cross Reference Table (Equivalent Grade) of Ti-6Al-2Sn-4Zr-2Mo Ti Alloy
| Grade | Standard | Country | Application |
|---|---|---|---|
| Q195 | China | Engineering and welding | |
| Q215 | China | Engineering and welding | |
| Q215 B | China | Engineering and welding | |
| Q235 | China | Engineering and welding | |
| Q235 B | China | Engineering and welding | |
| Q235 C | China | Engineering and welding | |
| Q235 D | China | Engineering and welding | |
| Q255 A | China | Engineering and welding | |
| Q255 B | China | Engineering and welding | |
| Q275 | China | Engineering and welding | |
| Q235q C | China | Bridge structure with steel | |
| Q235q D | China | Bridge structure with steel | |
| Q345q E | China | Bridge structure with steel | |
| Q345q C | China | Bridge structure with steel | |
| ASTM 1030 | ASTM | USA | General use carbon steel bar |
| UNS G10300 | UNS | USA | General use carbon steel bar |
| ASTM 1005 | ASTM | USA | General use carbon steel bar |
| UNS G10050 | UNS | USA | General use carbon steel bar |
| ASTM 1006 | ASTM | USA | General use carbon steel bar |
| UNS G10060 | UNS | USA | General use carbon steel bar |