Ti-13V-11Cr-3Al Ti Alloy
AISI Ti-13V-11Cr-3Al Ti Alloy Ti Alloy and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
| Category | Type | Steel Grade | Standard | Country | Application |
|---|---|---|---|---|---|
| Steel Grades | Ti Alloy | Ti-13V-11Cr-3Al Ti Alloy | AISI | ||
| Ti-6Al-2Sn-4Zr-2Mo Ti Alloy | |||||
| Ti-6Al-2Sn-2Zr-2Mo-2Cr-0.25Si Ti Alloy | |||||
| Ti-6Al-2Nb-1Ta-1Mo Ti Alloy | |||||
| Ti-5Al-5Sn-2Zr-2Mo-0.25Si Ti Alloy | |||||
| Ti-5Al-2.5Sn-ELI (low O2) Ti Alloy | |||||
| Ti-5Al-2.5Sn Ti Alloy | |||||
| Ti-5AI-2Sn-2Zr-4Mo-4Cr Ti Alloy | |||||
| Ti-3Al-8V-6Cr-4Mo-4Zr Ti Alloy | |||||
| Ti-3Al-2.5V Ti Alloy | |||||
| Ti-2.25-Al-11Sn-5Zr-1Mo-0.2Si Ti Alloy |
Chemical composition(mass fraction)(wt.%) of the Ti-13V-11Cr-3Al Ti Alloy
| Category | Titanium Alloy |
| Class | Wrought |
| Type | Beta alloy |
| Designations | United States: MIL-T-9046, AMS 4917 |
| Composition |
|
| Mechanical Properties |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 4.84 | 25 | |
| Poisson’s Ratio | 0.304 | 25 | |
| Elastic Modulus (GPa) | 101.4 | 25 | |
| Tensile Strength (Mpa) | 1276 | 25 | solution+age |
| Yield Strength (Mpa) | 1207 | ||
| Elongation (%) | 8 | ||
| Reduction in Area (%) | |||
| Hardness (HRC) | 40 | 25 | solution+age |
| Impact Strength (J) (Charpy) |
11 | 25 | solution+age |
| Thermal Properties |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Thermal Expansion (10-6/ºC) | 9.4 | 20–100 more | |
<script type=text/javascript>
</script><script src=”http://pagead2.googlesyndication.com/pagead/show_ads.js” type=text/javascript>
</script><script src=”http://pagead2.googlesyndication.com/pagead/js/r20120130/r20110914/show_ads_impl.js”></script><script src=”http://pagead2.googlesyndication.com/pagead/render_ads.js”></script><script>google_protectAndRun(“render_ads.js::google_render_ad”, google_handleError, google_render_ad);</script>
Mechanical Properties of steel grade Ti-13V-11Cr-3Al Ti Alloy
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 979 (≥) | 518 (≥) | 42 | 13 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 332 |
Physical Properties of steel grade Ti-13V-11Cr-3Al Ti Alloy
| Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
|---|---|---|---|---|---|---|---|
| 14 | – | – | 0.12 | – | |||
| 237 | 985 | – | 12.3 | 112 | – | ||
| 233 | – | 11 | 12.2 | 143 | 234 |
Heat Treatment of steel grade Ti-13V-11Cr-3Al Ti Alloy
Heat treated : 1517°C – 1623°C
Technological Curves of steel grade Ti-13V-11Cr-3Al Ti Alloy
No Curve
Cross Reference Table (Equivalent Grade) of Ti-13V-11Cr-3Al Ti Alloy
| Grade | Standard | Country | Application |
|---|---|---|---|
| Q195 | China | Engineering and welding | |
| Q215 | China | Engineering and welding | |
| Q215 B | China | Engineering and welding | |
| Q235 | China | Engineering and welding | |
| Q235 B | China | Engineering and welding | |
| Q235 C | China | Engineering and welding | |
| Q235 D | China | Engineering and welding | |
| Q255 A | China | Engineering and welding | |
| Q255 B | China | Engineering and welding | |
| Q275 | China | Engineering and welding | |
| Q235q C | China | Bridge structure with steel | |
| Q235q D | China | Bridge structure with steel | |
| Q345q E | China | Bridge structure with steel | |
| Q345q C | China | Bridge structure with steel | |
| ASTM 1030 | ASTM | USA | General use carbon steel bar |
| UNS G10300 | UNS | USA | General use carbon steel bar |
| ASTM 1005 | ASTM | USA | General use carbon steel bar |
| UNS G10050 | UNS | USA | General use carbon steel bar |
| ASTM 1006 | ASTM | USA | General use carbon steel bar |
| UNS G10060 | UNS | USA | General use carbon steel bar |