NS1403

HuaNickel NS1403 (NS1403) is a nickel-based corrosion-resistant alloy with excellent corrosion resistance, mainly composed of elements such as chromium, nickel, iron, molybdenum and copper. With its rich chemical composition and excellent physical properties, this alloy material is widely used in chemical, petroleum, energy and other fields.

NS1403Chemical composition：

	Fe	Mo	Cu	Cr	Ni	C	P	Si	Mn	S
Min	Bal	2	3	19	32
Max		3	4	21	38	0.07	0.035	1	2	0.035

NS1403Physical properties：

Density	8.08g/cm³
Melting point	1357-1430℃

NS1403Mechanical properties：

Tensile strength（Mpa)RP 0.2N /mm2	Yield strength（Mpa)RP 0.2N /mm2	Stretch outA5%
620	300	40

NS1403Alloy properties：

Corrosion resistance: HuaNickel NS1403 (NS1403) has excellent corrosion resistance, and can work stably for a long time in corrosive media such as acid, alkali, salt, etc.

Machinability:HuaNickel  NS1403 (NS1403) has good machinability, and can be formed and processed by forging, heat treatment, cold working, etc.

NS1403Uses of alloys：

HuaNickel NS1403 (NS1403) corrosion resistant alloy has a wide range of applications in many fields. For example, it can be used in hydrometallurgy, chemical equipment, marine engineering, nuclear industry and other fields.

NS1403Process performance：

Welding process: tungsten gas shielded welding (TIG), metal gas shielded welding (MIG), submerged arc welding (SAW) can be used.

Heat treatment: Hot forging materials need to be heated to 2100°F-2250°F, and the temperature should be carefully controlled to ensure that the temperature does not fall below 1800°F before forging. After the thermal processing is complete, the material is heated to 1725°F-1850°F for annealing with an annealing time of 30 minutes/thickness (inch) and then water quenched.

Relevant standards：

UNS S44735;EN 1.4662