GH4033

GH4033 is a nickel-based superalloy that is mainly composed of elements such as Ni-Cr. It has good antioxidant properties. HuaNickel GH4033 alloy has good cold and hot working properties. It is suitable for the production of turbine blades operating below 750°C and turbine discs operating below 700°C.

GH4033 Chemical composition：

	Ni	C	Cr	AI	Ti	Fe	B	Ce	Mn	Si	P	S	Cu
Min	Bal	0.03	19	0.6	2.4
Max		0.08	22	1	2.8	4	0.01	0.02	0.4	0.65	0.015	0.007	0.07

GH4033 Physical properties：

Density		8.20g/cm³
Resistivity	20℃	1.24×10~⁶Ω·m¹²
Magnetic properties		not

Coefficient of linear expansion

θ/℃	20～100	20～200	20～300	20～400	20～500
α/(10-6℃-I)	11.56	12.30	13.17	13.79	14.52
θ/℃	20～600	20～700	20～800	20～900	—
α/(10-6℃-I)	15.07	15.62	16.30	17.15

Resilient performance

θ/℃	20	100	200	300	400	500	600	700	800	900
Ed/GPa	221	217	212	205	198	192	184	177	167	160
E/GPa	206	—	—	—	—	—	159	150	127	—

GH4033 Mechanical properties：

Standard number	Variety/mm		Tensile properties					Roomtemperature performance		Long-lasting performance
			θ/℃	σb/MPa	σp0.2/MPa	δ₅/%	ψ/%	HBS	Aku/J	θ/℃	σ/MPa	τ/h
				≥					≥			≥
GJB1953AGB/T14993	For aviation rotating parts Hot rolled rods		700	685		15	20	321～255		700	430 (410)	60 (80)
HB 5198			700	735		15	20	321～255		700	451 (432)	40 (60)
GJB 3165A	Aviation load-bearing parts with hot rolled and Forged rods	d≥50	20	880	590	13	16	321～255	23.5	750	345 (295)	50  (100)
		d<50rods and flat lumber	700	685		15	20	311～255		700	430 (412)	60 (80)
YB/T 52452	Ordinary load-bearing partswith hot rolled and Forged rods	>d55	20	880	590	13	16	321～255		750	295	100
		<d20rods and flat lumber	700	685		15	20	311～255		700	430 (412)	60 (80)
GJB2611AGB/T14994	Cold drawer		700	685		15	20	—		700	430 (410)	60 (80)

GH4033 Alloy properties：

GH4033 alloy has a greater tendency to form uneven grains and coarse grains during hot rolling and forging, which is easy to produce coarse-grained waste. In addition, the production process should be strictly controlled to avoid a decrease in tensile plasticity at 700°C.

GH4033 Uses of alloys：

GH4033 alloy has been used in the manufacture of aero engine turbine working blades, turbine disks and other high-temperature load-bearing parts.

GH4033 Process performance：

Welding process: HuaNickel GH4033 alloy can be argon arc welding in the solution state, and should be treated in time after welding to eliminate welding stress.

Relevant standards：

GB/T14993、GB/T 14994、GB/T14997、GB/T14998、GJB1953A、GJB 2611A、GJB 2612A、GJB 3020A、GJB3165A、GJB 3782A 、GJB 5301 、HB 51、HB/Z140、YB/T 5245、QJ/DT01.63000   GH4033