GH3600

HuaNickel GH3600 is a Ni-Cr-Fe based solution-strengthened deformed superalloy, which has good thermal strength and high plasticity below 800°C, and good high temperature corrosion resistance and oxidation resistance below 1000°C. The alloy has a stable structure for long-term use, and has excellent cold and hot processing, welding properties and low temperature mechanical properties.

GH3600 Chemical composition：

	Ni	Cr	Fe	C	AI	Ti	Nb	Mn	Si	P	S	Cu
Min	—	14	6	—	—	—	—	—	—	—	—	—
Max	72	17	10	0.15	0.35	0.5	1	1	0.5	0.04	0.015	0.5

GH3600 Physical properties：

Density	8.43g/cm3
Melting point	1370~1430℃
Magnetic properties	not

GH3600 Mechanical properties：

Standard number	variety	heat treatment	θ/℃	Tensile properties				HBS
				σb/MPa	σp0.2/MPa	δ₅/%	ψ/%
				≥
辽新7-0110	Rods	(1000～1030)℃/AC	20	550	240	35	40
			900	95	85	65	50
辽新7-0065	Round cakes, ring blanks, ring pieces	1010℃/AC	20	520	205	35	—	187
辽新7-0004	Hot rolled thick plate	(1020～1040)℃/AC	20	550	240	35	40
			900	95	45	40	50
辽新7-0003	Cold-rolled sheet	(1010～1030)℃/AC	20	550	240	30
			900	90	40	60
Q/3B 4082	Cold-rolled strip	1010℃/AC	20	550	240	30

GH3600 Alloy properties：

Corrosion resistance: HuaNickelGH3600 alloy has good corrosion resistance in fresh water and flowing seawater, and corrosion spots may occur in still seawater. High corrosion resistance to various exhaust gases, alkaline solutions and most organic acids and compounds. It is not easy to produce stress corrosion cracks of chloride ions, but it is easy to produce stress corrosion cracks under the conditions of high concentration of caustic alkali or high-temperature mercury.

GH3600 Uses of alloys：

Alloys can be used to make rocket engine nozzle extensions, aero engine high-pressure compressors, static inner and outer rings, high-pressure guide blade orifice, sealing sheets, etc. And in the petrochemical, nuclear reactor, chemical food equipment and electronic components and other fields used in the production of exhaust pipes, carburizing containers, heat treatment equipment rollers, springs, heat exchanger pipes, reactor control rods and pipes and other parts.

GH3600 Process performance：

Welding process: the alloy welding performance is good, can be connected by various methods such as arc welding, argon arc welding, resistance welding and brazing, and large or complex welded structural parts should be annealed at 870 °C for 1h after fusion welding to eliminate welding stress.

Heat treatment: The parts are carried out according to the standard heat treatment system of the corresponding varieties. The annealing of sheet and strip parts should be carried out in a protective atmosphere. Heating and annealing should be carried out in a weakly reducing NOT sulfur atmosphere. The content of hydrogen and carbon monoxide in the reducing atmosphere is at least 2%, and bright annealing should be carried out in dry argon.

Relevant standards：

GB/T14992  、GJB 5060   GH3600  、辽新7-0003  GH600、辽新7-0004  GH600、辽新7-0065  GH600 、辽新7-0100  GH600 、辽新7-0110  GH600 、Q/5B4030 、Q/3B4082、Q/3B4083