2.4660

HuaNickel 2.4660 has excellent performance and is resistant to corrosion in chemical environments containing sulfuric acid and in environments containing chloride, nitric acid and phosphoric acid.

2.4660Chemical composition：

	Fe	Ni	Cr	Cu	Mo	C	Mn	P	S	Si
Min	Bal	32	19	3	2
Max		38	21	4	3	0.07	2	0.045	0.035	1

2.4660Physical properties：

Density		8.08g/cm3
Shear modulus		76GPa
Young’s modulus		193GPa
Specific heat		500J/kg･K
Resistivity		1.08μΩ･cm
Thermal conductivity		12.3W/m･K
Coefficient of expansion	25-100°C	14.7

2.4660Mechanical properties：

Tensile strength		Yield Strength (0.2% offset)		Elongation
Ksi	MPa	Ksi	MPa	%
90	620	45	300	40

2.4660Alloy properties：

Corrosion Resistance: HuaNickel 2.4660 exhibits excellent corrosion resistance in chemical environments containing sulfuric acid, chloride, phosphoric acid and nitric acid. This makes it very popular in the chemical, petrochemical, marine engineering, and other fields for the manufacture of reactors, heat exchangers, valves, etc.

High-temperature performance: The alloy is able to withstand temperatures up to 760-1175°C, which makes it suitable for high-temperature applications such as aerospace, power, and metallurgy. Especially in equipment that requires prolonged exposure to high temperatures, 2.4660 provides consistent performance.

Oxidation resistance:HuaNickel 2.4660 not only has good mechanical strength, but also effectively resists the oxidation process, thus extending its service life.

2.4660Uses of alloys：

It is mainly used in chemicals, petroleum, solvents, explosives, inorganic and organic chemicals, pharmaceuticals, food and synthetic materials. Nichrome 020 is manufactured in the production of mixing tanks, heat exchangers, process piping, pickling equipment, pumps, valves, fasteners and fittings.

2.4660Process performance：

Welding process: 2.4660 alloy can be welded with the same material or other metals by traditional welding processes, such as tungsten electrode inert gas welding, plasma arc welding, manual sub-arc welding, metal pole inert gas shielded welding.

Heat Treatment Process: The thermoforming range should be in the range of 1400-2150°F (760-1175°C). Nickel alloy alloy 020 is usually used under annealed conditions.

Relevant standards：

Rod, Bar, Wire and Forging Stock – ASTM B 462 ASTM B 472, ASTM B 473, ASME SB 472, ASME SB 473, ISO

9723, ISO 9724, ISO 9725, DIN 17752-17754

Plate, Sheet and Strip – ASTM A 240, ASTM A 480, ASTM B 463, ASTM B 906, ASME SA 240, ASME SA 480, ASME

SB 463, ASME SB 906, ISO 6208, DIN 17750

Pipe and Tube – ASTM B 729, ASTM B 829, ASTM B 468, ASTM B 751, ASTM B 464, ASTM B 775, ASTM B 474,

ASME SB 729, ASME SB 829, ASME SB 468, ASME SB 751, ASME SB 464, ASME SB 775, ASME SB 474, ISO 6207,

DIN 77751

Other – DIN 17744, ASTM B 366, ASTM B 462, ASTM B 471, ASTM B 475, ASME SB 366, ASME SB-462, ASME SB

471, ASME SB 475