1.4501

In the early days (early 80s of the 20th century), this steel was used as cast steel to replace the second-generation duplex stainless steel 00Cr22Ni5Mo2N (2205) with insufficient corrosion resistance. In the late 80s, it began to be used as a texturing material for pipeline systems, and subsequently became an important corrosion-resistant material for oil and gas development, seawater environments, flue gas desulfurization (FGD), desalination, chemical and other applications.

1.4501 Chemical composition：

	Cr	Ni	Mo	N	Cu	C	Si	Mn	S	P
Min	24	6	3	0.2	0.5	≤
Max	26	8	4	0.3	1	0.03	1	1	0.02	0.035

1.4501 Physical properties：

Densityg/g·cm-3	Specific heat capacity/J·(kg·K)-1	Resistivity /10-6Ω ·m	Young’s modulus of elasticity/GPa
7.84	–	0.85	19

1.4501 Mechanical properties：

Plate thickness/mm	db/MPa	do.2/MPa	δs/%	hardness(HRC)	Impact value (V-type)Akv/J
					20℃	-30℃
10	874	671	734	42	241	207
12	865	690	737	38	227	227
19	843	647	701	40	211	183
34	853	627	700	32	241	248

1.4501 Alloy properties：

Like other super duplex stainless steels, the microstructure of this steel is also a duplex structure with a α/γ close to 1 under solution conditions, but there will also be intermetallic phases and nitride precipitation on the steel matrix during cooling from high temperature to room temperature, including incorrect heat working, heat treatment and welding processes.

1.4501 Uses of alloys：

HuaNickel 1.4501 is mainly used for offshore oil and gas exploitation, in the power station flue gas desulfurization, petrochemical engineering and fertilizer industry, the manufacture of reactors, containers, various heat exchangers, pipelines, pumps, valves, etc.

1.4501 Process performance：

Soldering process: Soldering is performed using SMAW, GTAW and SAW methods.

Heat treatment: HuaNickel1.4501  suitable heat treatment temperature is 1000~1100 °C, fast cooling after heat preservation.

Relevant standards：ASTM A1082/A1082M -2016