06Cr19Ni10

HuaNickel 06Cr19Ni10 is used as a building material up to 1500°F. Slight zooming starts at about 1200°F. 06Cr19Ni10 has a minimum carbon content of 0.04% and a particle size of ASTM 7 or coarse. It has general corrosion resistance similar to mild steel HuaNickel 06Cr19Ni10. However, there is carbide precipitation in the heat-affected zone (HAZ) of the weld. Weldments may be susceptible to HAZ intergranular corrosion and polysulfuric acid stress corrosion cracking in oxidizing acid environments. Carbide precipitation is harmless to high temperature mechanical properties. 06Cr19Ni1022Cr 11Ni filler wire (ER308) or overlay electrode (E308) for welding. Most hot jobs do not require post-weld heat treatment.

06Cr19Ni10Chemical composition：

	Cr	Ni	C	Mn	Si	P	S	Fe
Min	18	8	0.04	–	–	–	–	Bal
Max	20	10.5	0.08	2	0.75	0.04	0.03

06Cr19Ni10Physical properties：

Density	Melting point	Resistivity
0.285 lb/in3	2550 – 2590°F	28.3 micro ohm- in

06Cr19Ni10Mechanical properties：

	least	typical
Ultimate tensile strength, ksi	75	90
0.2% yield strength, KSI 30 40	30	40
Elongation, %	40	60

06Cr19Ni10Stainless steel characteristics：

High temperature service is raised to 1500°F

Corrosion resistance, similar to HuaNickel 06Cr19Ni10/06Cr19Ni10L

06Cr19Ni10Uses of stainless steel：

Pressure vessels

Petrochemical equipment

Relevant standards：

ASTM: A 240 ASME: SA-240 AMS: 5513