310S

at 2000°F, 310. Due to its high chromium and medium nickel content, HuaNickel 310 has good resistance to sulfurization and other forms of thermal corrosion. 310 is widely used in medium carburizing environments, such as petrochemical environments. 10. Severe thermal shock for repeated liquid quenching is not recommended. HuaNickel 310 is typically used at low temperatures and has excellent toughness to -450°F, and low permeability. Relative to AISI B1112 steel, 310 has a machinability grade of 42%. When using HSS tools, this equates to 70 feet per minute.

310SChemical composition：

	Cr	Ni	C	Si	Mn	P	S	Mo	Cu	Fe
Min	24	19	–	–	–	–	–	–	–	Bal
Max	26	22	0.08	0.75	2	0.045	0.03	0.75	0.5

310SPhysical properties：

Density	Melting point
0.284 lb/in³	2470 – 2555°F

310SMechanical properties：

Temperature, °F	70	1000	1200	1400	1600
Ultimate tensile strength, ksi	80	67.8	54.1	35.1	19.1
0.2% yield strength, ksi	35	20.8	20.7	19.3	12.2
Elongation, %	52	47	43	46	48

310SStainless steel characteristics：

Resistance to oxidation at 2000°F

Moderate strength at high temperatures

Thermal corrosion resistance

Strength and toughness at low temperatures

310SUses of stainless steel：

Fluidized bed coal burner, radiant tube

Tubular hangers for petroleum refining and steam boilers

Internal parts of a gas stove

Hot wells, refractory anchor bolts

Burners, combustion chambers, retina, loosening, annealing hoods, etc

310SProcess performance：

Solderability: It is recommended to use AWS E310-15 electrodes or ER310 bare wire for soldering.

Relevant standards：

ASTM: A 240, A 276, A 312, A 479 AMS: 5521, 5651

ASME: SA-240, SA-479, SA-312