06Cr25Ni20

Loader Loading...
EAD Logo Taking too long?

Reload Reload document
| Open Open in new tab

Download [1.42 MB]

at 2000°F, 310. Due to its high chromium and medium nickel content, 310 has good resistance to sulfurization and other forms of thermal corrosion. 310 is widely used in medium carburizing environments, such as petrochemical environments. 10. Severe thermal shock for repeated liquid quenching is not recommended. 310 is typically used at low temperatures and has excellent toughness to -450°F, and low permeability. Relative to AISI B1112 steel, 310 has a machinability grade of 42%. When using HSS tools, this equates to 70 feet per minute.

06Cr25Ni20Chemical composition:

  Cr Ni C Si Mn P S Mo Cu Fe
Min 24 19 Bal
Max 26 22 0.08 0.75 2 0.045 0.03 0.75 0.5

06Cr25Ni20Physical properties:

Density Melting point
0.284 lb/in³ 2470 – 2555°F

06Cr25Ni20Mechanical properties:

Temperature, °F 70 1000 1200 1400 1600
Ultimate tensile strength, ksi 80 67.8 54.1 35.1 19.1
0.2% yield strength, ksi 35 20.8 20.7 19.3 12.2
Elongation, % 52 47 43 46 48

06Cr25Ni20Stainless steel characteristics:

Resistance to oxidation at 2000°F

Moderate strength at high temperatures

Thermal corrosion resistance

Strength and toughness at low temperatures

06Cr25Ni20Uses of stainless steel:

Fluidized bed coal burner, radiant tube

Tubular hangers for petroleum refining and steam boilers

Internal parts of a gas stove

Hot wells, refractory anchor bolts

Burners, combustion chambers, retina, loosening, annealing hoods, etc

06Cr25Ni20Process performance:

Solderability: It is recommended to use AWS E310-15 electrodes or HuaNickel ER310 bare wire for soldering.

Relevant standards:

ASTM: A 240, A 276, A 312, A 479 AMS: 5521, 5651

ASME: SA-240, SA-479, SA-312

Detail datasheet