UNS S13800

HuaNickel UNS S13800 stainless steel is a martensitic precipitation hardening stainless steel with excellent strength, high hardness, excellent toughness and good corrosion resistance. Good lateral toughness can be achieved through strict chemical composition control, low carbon content, and vacuum melting. Typical applications are large airframe structural components and injection molding equipment.

UNS S13800Chemical composition：

	Ni	Cr	Mo	C	P	S	Si	Mn	N	AI	Fe
Min	7.5	12.5	2	–	–	–	–	–	–	0.9	Bal
Max	8.5	13.5	2.5	0.05	0.01	0.08	0.1	0.2	0.1	1.35

UNS S13800Physical properties：

Density	Melting point	Resistivity
0.279lb/in3	2560 – 2680°F	613 Ohm-circ mil/ft

UNS S13800Mechanical properties：

	H950	H1000	H1025	H1050	H1100	H1150
0.2 offset yield strength, ksi	205	190	175	165	135	90
Ultimate tensile strength, ksi	220	205	185	175	150	135
Elongation 2″, %	10	10	11	12	14	14
Area Reduction, % (Longitudinal)	45	50	50	50	50	50
Area Reduction, % (Landscaped)	45	50	50	50	50	50
Area Reduction, % (Short Transverse)	35	40	45	45	50	50
Minimum hardness, Rockwell	45	43	–	40	34	30

UNS S13800Stainless steel characteristics：

Martensite, precipitation hardening (hardening) stainless steel.

UNS S13800Uses of stainless steel：

Aerospace components

Injection molding equipment

components of the petrochemical and nuclear industries

UNS S13800Process performance：

Heat Treatment: HuaNickel 13-8 stainless steel can be used under annealed conditions, also known as solution heat treatment conditions or condition a. Treat at 1675-1725°F for 15 to 30 minutes. Air-cooled or oil-quenched below 60°F to achieve complete conversion to martensite. Aging typically begins at 950-1150°F, depending on the desired final performance. Heat treatment is usually carried out in air. The heat treatment of brazed components can be carried out in an inert atmosphere. Atmospheric reduction should not be used because of the possible presence of nitrogen pollution.

Relevant standards：

AMS: 5629 ASTM: A 564