00Cr24Ni22Mo7Mn3CuN

HuaNickel 00Cr24Ni22Mo7Mn3CuN steel series is based on the aforementioned 00Cr20Ni18Mo6CuN steel to increase chromium. A 7Mo type super austenitic stainless steel developed by nickel and molybdenum. The PRE value (Pitting Resistance Equivalent Value) of this steel is as high as 55. The nitrogen content in steel can reach about 0.5%, which is almost the highest amount of dissolved nitrogen at atmospheric pressure for stainless steel with high chromium (about 24%) and low manganese (about 3%). This steel has excellent resistance to various types of corrosion, and can replace iron-nickel-based or even nickel-based corrosion-resistant alloys in many media, thus filling the gap between stainless steel and high-nickel corrosion-resistant alloys without high pitting resistance and high crevice corrosion resistance stainless steel.

00Cr24Ni22Mo7Mn3CuN Chemical composition：

	Mn	Cr	Ni	Mo	Cu	N	C	Si	P	S
Min	2	24	21	7	0.45	0.45	≤
Max	4	25	23	8	0.55	0.55	0.02	0.5	0.03	0.003

00Cr24Ni22Mo7Mn3CuN Physical properties：

Density/g · cm-3	Specific heat capacity/J · (kg·K)-1	Resistivity /μΩ ·m	Young’s elasticity modulus/GPa	Thermal conductivity/W·(m·℃)-1
				20℃	100℃	200℃	300℃	400℃
8.00	510	0.78	188	8.6	9.8	11.3	12.6	14.5

00Cr24Ni22Mo7Mn3CuNMechanical properties：

Mechanical properties
σb/MPa	σp0.2/MPa	δ/%	Impact power/J
			20℃	-196℃
≥750	≥410	≥40	250	125

00Cr24Ni22Mo7Mn3CuN Alloy properties：

HuaNickel 00Cr24Ni22Mo7Mn3CuN steel has a single austenitic structure in its solid solution, which is the same as 6% Mo type super austenitic stainless steel. Because this steel belongs to 7% Mo section steel and the amount of chromium, molybdenum and nitrogen in the steel is very high, when the heat working, hot forming and heat treatment, welding and other processes are not suitable, it is more likely to have intermetallic phase and Cr₂N precipitation on the matrix, thereby damaging various properties of steel, especially plasticity, toughness and corrosion resistance.

00Cr24Ni22Mo7Mn3CuNUses of alloys：

00Cr24Ni22Mo7Mn3CuN is mostly used in equipment, components, containers, heat exchangers and pipelines used in flue gas purification environments such as chemical industry, seawater, paper industry and flue gas desulfurization (FGD).

00Cr24Ni22Mo7Mn3CuNProcess performance：

Welding process: The welding performance of this steel is good. It can be welded using the same welding method used in austenitic stainless steels. For manual arc welding, P16 electrodes are recommended.

Heat treatment: The suitable heat treatment process of HuaNickel 00Cr24Ni22Mo7Mn3CuN steel is ≥ 1150°C heating and heat preservation and fast cooling.

Relevant standards：

ASTM A240/A240M-2020