HuaNickel Alloy C2000 alloy is a high-performance nickel-based alloy with excellent corrosion resistance. It is widely used in aerospace, petrochemical, nuclear power generation and other fields.

Alloy C2000Chemical composition:

  Ni Cr Mo Cu C Si Mn P S Fe AI Co
Min Bal 22 15 1.3
Max 24 17 1.9 0.01 0.08 0.5 0.04 0.02 3 0.5 2

Alloy C2000Physical properties:

Density/g·cm-3 Linear expansion coefficient/×10-6·K-1 25~100℃ Thermal conductivity/W·(m·K)-1 room temperature Resistivity/μΩ ·mroom temperature
8.5 12.4 9.1 1.28

Alloy C2000Mechanical properties:

Plate thickness/mm σb/MPa σpo.2/MPa δ(50mm)/%
1.6 752 358 64
3.2 765 393 63
6.4 779 379 62
13 758 345 68
25 752 372 63

Alloy C2000Alloy properties:

The solid solution state of HuaNickel Alloy C2000 alloy is also an austenite structure with a face-centered cubic crystal structure, while in the medium-temperature heating (sensitization, aging) state, there will be carbide and intermetallic phase precipitation.

Alloy C2000Uses of alloys:

This alloy is suitable for the manufacture of various forms of corrosion-resistant devices and components, including towers, tanks, reactors, heat exchangers, pipelines and pipe fittings, as well as forgings, pumps, valves, etc.

Alloy C2000Process performance:

Welding performance: Manual arc welding (SMAW), tungsten argon arc welding (GTAW) and gas arc welding (GMAW) are recommended, but oxyacetylene welding and submerged arc welding are not recommended.

Heat treatment: HuaNickel Alloy C2000 alloy is also solution treated, the suitable heating temperature is about 1150 °C, water cooling after heat preservation, for Ni-Cr-Mo type alloys, the stress relief after welding can not be carried out in the sensitization temperature range, in order to eliminate the residual stress must also be solution treatment.

Relevant standards:

ASTM B574、 ASTM B575、 ASTM B622、 ASTM B619 、ASTM B626 、ASTM B564