1Cr18Ni11SiA1Ti
China GBT 1Cr18Ni11SiA1Ti Austenite-Ferrite and 1Cr18Ni11SiA1Ti Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
| Category | Type | Steel Grade | Standard | Country | Application |
|---|---|---|---|---|---|
| Steel Grades | Special Steel | 1Cr18Ni11SiA1Ti | GBT | China | Austenite-Ferrite |
| G-X 12 Cr 13 | |||||
| G-X 6 CrNi 13 4 | |||||
| G-X 8 CrNi 19 9 | |||||
| 26NiCrMoV14-5 / 1.6957 / HW19476 | |||||
| ASTM A 565 GR 616 | |||||
| S42200 | |||||
| 442S19 | |||||
| MIL S 861 | |||||
| AISI 414 | |||||
| 0Cr26Ni5Mo2 |
Chemical composition(mass fraction)(wt.%) of the 1Cr18Ni11SiA1Ti
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Other(%) |
|---|---|---|---|---|---|---|---|
| 0.10-0.18 | 3.40-4.00 | Max 0.80 | 0.035 | Max 0.03 | 17.50-19.50 | 10.00-12.00 | Al 0.10-0.30;Ti 0.40-0.70 |
Mechanical Properties of steel grade 1Cr18Ni11SiA1Ti
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 184 (≥) | 175 (≥) | 11 | 24 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 133 |
Physical Properties of steel grade 1Cr18Ni11SiA1Ti
| Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
|---|---|---|---|---|---|---|---|
| 21 | – | – | 0.43 | – | |||
| 724 | 268 | – | 31.3 | 243 | – | ||
| 771 | – | 13 | 34.2 | 233 | 234 |
Heat Treatment of steel grade 1Cr18Ni11SiA1Ti
Heat treated : 1663°C – 1838°C
Technological Curves of steel grade 1Cr18Ni11SiA1Ti
No Curve
Cross Reference Table (Equivalent Grade) of 1Cr18Ni11SiA1Ti
| Grade | Standard | Country | Application |
|---|---|---|---|
| 1Cr18Ni11SiA1Ti | GBT | China | Austenite-Ferrite |